Water Based Acrylic Anticorrosive Finish

[Search Related Products]

Water Based Acrylic Anticorrosive Finish

Water Based Acrylic Anticorrosive Finish

Feature£ºIt can quickly dry in normal temperature with good adhesion. It has good anticorrosion. It should contact with water in 36 hours after dry. It is not poisonous and polluted. It can dilute with water. Good water property after form film.

Usage: It is used to different metal surface as anticorrosion primer.

Technical parameter£º

Mixing ratio£ºsingle pack
Typical film thickness£ºdry coat: 30¦Ìm/coat
Spreading rate£º0.1kg/©O/30¦Ìm
Solid content£º60%h
Humidity£ºbelow 85%
Coating interval

Temperature £¨¡æ£©

10

20

30

Dry to touch£¨hrs£©

60

45

30

Dry semi-hard£¨hrs£©

28

20

8

Min. interval£¨hrs£©

28

20

8

Composition£ºIt is made of water-based epoxy modified acrylic resin and anticorrosion pigment, add with additives. Packed in single.

Matching£º

Substrate: Nake steel, zinc steel, aluminum steel, stainless steel.

Upper coating: Many anticorrosion finish

Application of Water Based Acrylic Anticorrosive Finish:
Water Based Acrylic Anticorrosive Finish

Water Based Acrylic Anticorrosive Finish

Contact with us now

Our mail: manager@hiseamarine.com